英國進口MWA鑄鐵焊條Mac Cast E407 S|ENiFe-CI HR|鑄鐵和鋼焊接
Manufactured on a pure nickel core wire with an extruded basic flux containing both graphite and a high bllurgical grade of iron powder. Welds with a soft stable arc and ensures a bl recovery of 160% with respect to core wire. Designed for welding all grades of cast iron to steel. The advanced deoxidisation system ensures the maximum combination of weld strength, ductility and machinability. The design principle of the electrode prevents overheating and provides great resistance to porosity.
Mac Cast E407S鑄鐵焊條采用純鎳焊芯及含有石墨和高冶金級鐵粉的擠壓堿性焊劑。軟穩(wěn)定電弧焊接，相對于焊芯的金屬回收率為160%。設(shè)計用于將所有等級的鑄鐵焊接到鋼上。先進的脫氧系統(tǒng)確保了焊縫強度、延展性和可加工性的最大結(jié)合。焊條的設(shè)計原理防止了過熱，并提供了極大的抗氣孔性能。
Typical All Weld Metal Chemical Analysis (%)
典型全焊縫金屬成分(%)
|
C |
Fe |
Mn |
Ni |
P |
S |
Si |
|
0.90 |
44.0 |
1.10 |
54.0 |
0.009 |
0.010 |
0.60 |
Typical All Weld Metal Mechanical Properties（As Welded）
典型全焊縫金屬機械性能（焊態(tài)）：
Tensile Strength抗拉強度： 410 N/mm2
0.2% Proof Stress屈服強度： 230 N/mm2
Elongation延伸率： 15%
Hardness硬度： 240 HV
Sizes Available and Recommended Amperages
尺寸Φ/電流：
|
2.5mm |
3.2mm |
4.0mm |
5.0mm |
|
70-100A |
100-130A |
140-190A |
180-220A |
Current電流：AC/DC (+/-)
Related Specification參考標(biāo)準(zhǔn)：AWS A5.15 ENiFe-CI HR
Storage儲存：Electrodes should be stored in dry conditions. Should the electrodes become damp, re-dry for one hour at 150°C before use. 焊條應(yīng)儲存在干燥環(huán)境中。如果焊條受潮，應(yīng)在150°C下重新干燥1小時后再使用。