| PC/ABS C1200 美國通用電氣公司 物性數(shù)據(jù) |
| 規(guī)格級(jí)別： | --- | 外觀顏色： | --- |
| 用途概述： | --- | ||
| 備注說明： | 特性：耐高溫及沖擊 | ||
| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 物理性能 | 比重 | --- | ASTM D-792 | 1.15 | --- |
| 吸水率 | --- | ASTM D-570 | - | % | |
| 模具收縮率 | 3.2mm | ASTM D-955 | 5-7 | E-3 | |
| 機(jī)械性能 | 拉伸強(qiáng)度(屈伏點(diǎn)) | --- | ASTM D-638 | 61 | Mpa |
| 拉伸模量 | --- | ASTM D-638 | 2274 | Mpa | |
| 彎曲強(qiáng)度 | --- | ASTM D-790 | 88 | Mpa | |
| 彎曲模量 | --- | ASTM D-790 | 2343 | Mpa | |
| 沖擊強(qiáng)度缺口 | 23℃ | ASTM D-256 | 640 | J/m | |
| 洛氏硬度 | --- | ASTM D-785 | - | R | |
| 電氣性能 | 拉伸率(斷裂點(diǎn)) | --- | ASTM D-638 | 150 | % |
| 損耗因數(shù) | 1MHz | ASTM D-150 | - | --- | |
| 介電常數(shù) | 1MHz | ASTM D-150 | - | --- | |
| 體積電阻 | --- | ASTM D-257 | - | Ohm-cm | |
| 表面電阻 | --- | ASTM D-257 | - | Ohm-cm | |
| 熱 性 能 | 阻燃性 | --- | UL-94 | HB | --- |
| 阻燃性 | --- | UL-94 | 1.6 | mm | |
| 熱變形溫度 | 0.45Mpa | ASTM D-648 | 129 | ℃ | |
| 熱變形溫度 | 1.8Mpa | ASTM D-648 | 112 | ℃ | |
| 維卡軟化點(diǎn) | --- | ASTM D-1525 | - | ℃ | |
| 線膨脹系數(shù) | 1/℃ | E-831 | 7.2E-05 | --- | |
| UL長期使用溫度 | 含沖擊 | UL-746B | 60 | ℃ | |
| UL長期使用溫度 | 無沖擊 | UL-746B | 60 | ℃ | |
PC/ABS結(jié)合了兩種材料的優(yōu)異特性，
ABS材料的成型性和PC的機(jī)械性、沖擊強(qiáng)度和耐溫、抗紫外線（UV）等性質(zhì)，可廣泛使用在汽車內(nèi)部零件、事務(wù)機(jī)器、通信器材、家電用品及照明設(shè)備上。[1][2]
典型應(yīng)用范圍:手機(jī)外殼、計(jì)算機(jī)和商業(yè)機(jī)器殼體、電器設(shè)備、草坪園藝機(jī)器、汽車零件儀表板、內(nèi)部裝修以及車輪蓋）。
注塑模工藝條件:干燥處理：加工前的干燥處理是必須的。濕度應(yīng)小于0.04%，建議干燥條件為90~110C，2~4小時(shí)。熔化溫度： 230~300C。模具溫度：50~100C。注射壓力：取決于塑件。注射速度：盡可能地高。
化學(xué)和物理特性: PC/ABS具有PC和ABS兩者的綜合特性。例如ABS的易加工特性和PC的優(yōu)良機(jī)械特性和熱穩(wěn)定性。二者的比率將影響PC/ABS材料的熱穩(wěn)定性。PC/ABS這種混合材料還顯示了優(yōu)異的流動(dòng)特性。收縮率在0.5%左右。
二、PC/ABS是一種通過混煉后合成的改性工程塑料。這種改性塑料比單純的PC和ABS性能更好，例如：抗沖擊性提高，耐熱性提高，硬度提高等等.
PC/ABS塑料 特點(diǎn)：
1、綜合性能較好,沖擊強(qiáng)度較高,化學(xué)穩(wěn)定性,電性能良好.
2、與372有機(jī)玻璃的熔接性良好,制成雙色塑件,且可表面鍍鉻,噴漆處理.
3、有高抗沖、高耐熱、阻燃、增強(qiáng)、透明等級(jí)別。
4、流動(dòng)性比HIPS差一點(diǎn)，比PMMA、PC等好，柔韌性好。