電解碳化鎢粉
Electrolysis Tungsten Carbide Powder
一、典型應(yīng)用Typical Applications
電解碳化鎢是將廢合金通過電解工藝生產(chǎn)出來的再生碳化鎢原料。 由于鎢資源有限，目前國家已經(jīng)開始調(diào)控，電解碳化鎢因為其生產(chǎn)能耗低，原料的適應(yīng)面廣，對于資源的再利用具有重要意義。
主要應(yīng)用于，硬質(zhì)合金，超硬材料，金剛石工具，焊接，耐高溫材料，鉆頭，各種硬質(zhì)合金刀具。
Electrolysis tungsten carbide is produced through the electrolysis process quality recycled scrap tungsten carbide materials. Electrolysis is low energy consumption, wide adaptability of raw materials, and great significance for the resource utilization.
Widely used in tungsten carbide, super-hard materials, diamond tools, welding, high temperature materials, drill bits, cutting tools etc.
二、主要物理特性Main Physical Specifications
過篩粒度/Particle Size: 60~325目(Mesh) 霍爾流速/Hall Flow Rate: 9~12 S/50g
松裝密度/Apparent Density: >6.8g/cm3 費氏粒度（FSSS）: 0.8~10.0μm
振實密度/Vibrating Density: >8.2g/cm3 外觀/Appearance: 深灰色/Dark Grey
|
牌號Grade |
EWC20 |
EWC50 |
EWC90 |
EWC10 |
|
|
主要成分（%） Main Contents |
總碳 Total C |
5.95~6.05 |
5.95~6.10 |
6.0~6.15 |
5.95~6.05 |
|
游離碳Free C |
0.05 |
0.05 |
0.04 |
0.04 |
|
|
雜質(zhì)含量%不大于 Impurity Content % Max |
O |
0.5 |
0.15 |
0.15 |
0.15 |
|
Ti |
0.5 |
0.1 |
0.05 |
0.05 |
|
|
Co |
0.3 |
0.3 |
0.3 |
0.3 |
|
|
費氏粒度(FSSS) |
1.6~3.2μm |
4.5~6.0μm |
8.0~10.0μm |
0.8~1.7μm |
|
|
推薦用途 Recommended Applications |
用途生產(chǎn)普通YG類，或者YT類硬質(zhì)合金產(chǎn)品
|
中顆粒度較粗的產(chǎn)品，適合大多數(shù)硬質(zhì)合金產(chǎn)品應(yīng)用 |
粗顆粒，主要應(yīng)用于地礦產(chǎn)品，如釬片 |
細顆粒，可以用于要求較高的硬質(zhì)合金產(chǎn)品，如圓棒、刀具等精加工產(chǎn)品 |
|
包裝：內(nèi)襯兩層塑料袋、外鐵桶，每桶50kg。
注：如客戶另有特殊要求，可具體洽談。Note：Another special requirements, specific negotiations
主要產(chǎn)品：質(zhì)合金原材料,鎢粉， 復(fù)式碳化物粉末（CK料、碳化鈦、氮碳化鈦、碳化鈮、碳化鉭、碳化鉻、碳化鉬、碳化釩、坦鈮固溶體、鈦鉭鎢固溶體粉末）；YT/YG混合料（原生/再生）；電解碳化鎢粉末；粗晶粒碳化鎢粉末等。