| EN ISO 3581-A. |
| E 19 12 3 L B 2 2 |
| SFA/AWS A5.4 |
| E316L-15 |
| 測試溫度(焊態(tài)) | +20 °C |
| 結(jié)果(焊態(tài)) | 95 J |
| 測試溫度(焊態(tài)) | -60 °C |
| 結(jié)果(焊態(tài)) | 75 J |
| 伸長率(焊態(tài)) | 30 % |
| 屈服強度(焊態(tài)) | 430 MPa |
| 抗拉強度(焊態(tài)) | 520 MPa |
| 電流類型 CA/CD/CC (+)(-) | DC+ |
| 硬度 (HRC) | 190-215 HV |
| 元素 | C |
| 額定百分比 | 0.04 % |
| 元素 | Si |
| 額定百分比 | 0.45 % |
OK 63.35 is a low carbon stainless steel electrode with basic coating of the 18Cr12Ni3Mo type. It is suitable for applications where the mechanical requirements are tough. It provides good impact toughness levels. Minimum lateral expansion of 0.38mm requirement is met down to -120°C. The same requirement can be met at -196°C when the ferrite content is at the low end of the specification i.e. FN 3 - 4.