| 特 性 | 高鉻成份,耐磨耗耐龜裂性能優(yōu)良,焊后硬度較高,機(jī)械加工困難. High chrome component, abrasion resistance, resistance to crack excellent perbance after welding, machining difficulty high hardness. |
| 用 途 | 淬火硬化模具鋼刃口的修補(bǔ),適用于SKD11合金工具鋼,淬火后的模具鋼修補(bǔ). Quench hardened steel blade of repair, applicable to SKD11 alloy steel, alloy after quenching repair. |
| 規(guī) 格 | 2.6￠ 3.2￠ 4.0￠ |
| 特 性 | 可直接在鑄鐵上施焊,對(duì)于抗冷沖壓的金屬間磨耗非常有效.焊金第一層為奧氏體組織,從第二層開(kāi)始為馬氏體組織抗磨耗性好. Can directly in the iron welding process, to make cold stamping bl abrasion very effective. Welding between the first layer of gold for austenitic group, second start martensite organization for good abrasion resistanceHRC46~52 |
| 用 途 | 球墨鑄鐵,火焰淬火鑄鐵,合金鑄鐵的直接堆焊. Ductile iron, flame hardening, alloy iron direct hardfacing. |
| 規(guī) 格 | 2.6￠ 3.2￠ 4.0￠ 5.0￠ |
| 特 性 | 可直接在鑄鐵上施焊,對(duì)于抗冷沖壓的金屬間磨耗非常有效.焊金第一層為奧氏體組織,從第二層開(kāi)始為馬氏體組織,抗磨耗沖壓性能優(yōu)良. Can directly in the iron welding process, to make cold stamping bl abrasion very effective. Welding between the first layer of gold for austenitic group, second began to martensitic organization, abrasion resistance stamping excellent perbance藍(lán)翔牌焊材 |
| 用 途 | 主要用于各種淬火后鑄鐵的刃口修補(bǔ)焊接. Mainly used for various hardened iron blade repair welding. |