Hostab® S 9364 XAP2 ?
聚甲醛(POM)共聚物
Celanese Corporation
產(chǎn)品說明:
Hostab® acetal copolymer grade S 9364 XAP2 ? is highly impact modified grade for demanding applications. Hostab® S 9364 XAP2 ? provides a significant improvement in impact strength and flexibility over standard impact modified grades such as Hostab® S 9063 and S 9064, and also exhibits exceptional low emission perbance meeting or exceeding the requirements of many automotive markets.
Chemical abbreviation according to ISO 1043-1: POM-HI
添加劑 |
沖擊改性劑 |
|||||
特性 |
|
|||||
用途 |
汽車領(lǐng)域的應(yīng)用 |
|||||
RoHS 合規(guī)性 |
聯(lián)系制造商 |
|||||
樹脂ID (ISO 1043) |
POM-HI |
|||||
物理性能 |
額定值 |
單位制 |
測試方法 |
|||
密度 |
1.37 |
g/cm3 |
ISO 1183 |
|||
溶化體積流率(MVR) (190°C/2.16 kg) |
4.00 |
cm3/10min |
ISO 1133 |
|||
收縮率 |
|
|
ISO 294-4 |
|||
橫向流量 |
1.5 |
% |
|
|||
流量 |
1.6 |
% |
|
|||
吸水率 (飽和, 23°C) |
0.80 |
% |
ISO 62 |
機(jī)械性能 |
額定值 |
單位制 |
測試方法 |
拉伸模量 |
1650 |
MPa |
ISO 527-2/1A/1 |
拉伸應(yīng)力 (屈服) |
43.0 |
MPa |
ISO 527-2/1A/50 |
拉伸應(yīng)變 (屈服) |
16 |
% |
ISO 527-2/1A/50 |
彎曲模量 (23°C) |
1550 |
MPa |
ISO 178 |
沖擊性能 |
額定值 |
單位制 |
測試方法 |
簡支梁缺口沖擊強(qiáng)度 |
|
|
ISO 179/1eA |
-30°C |
11 |
kJ/m2 |
|
23°C |
21 |
kJ/m2 |
|
簡支梁無缺口沖擊強(qiáng)度 |
|
|
ISO 179/1eU |
-30°C |
無斷裂 |
|
|
23°C |
無斷裂 |
|
|
熱性能 |
額定值 |
單位制 |
測試方法 |
熱變形溫度 |
|
|
|
0.45 MPa, 未退火 |
140 |
°C |
ISO 75-2/B |
1.8 MPa, 未退火 |
75.0 |
°C |
ISO 75-2/A |
熔融溫度 2 |
166 |
°C |
ISO 11357-3 |
線形熱膨脹系數(shù) |
|
|
ISO 11359-2 |
流動(dòng) |
1.2E-4 |
cm/cm/°C |
|
橫向 |
1.1E-4 |
cm/cm/°C |
|
|